Thermal stability of bimodal microstructure in magnesium alloy AZ91 processed by ECAP

Typ

článek v časopise ve Web of Science, Jimp

Jazyk

en

Originální abstrakt

The changes in microstructure of equal channel angular pressing (ECAP) processed magnesium alloy AZ91 during thermal exposure were studied in this paper. The microstructure stability was investigated by means of electron backscatter diffraction (EBSD), which allowed measuring the changes in grain size, mutual ratio of low-angle boundaries (LABs) to high-angle ones (HABs) and local lattice distortion evaluated by the kernel average misorientation (KAM) parameter. It was found experimentally that the threshold temperature at which significant grain coarsening takes place is 350 centigrade. No modification to mean grain diameter occur below this temperature, nonetheless, some changes in LAB and HAB fraction, as well as in local lattice distortion, can be observed.

Český abstrakt

Článek popisuje výsledky zkoumání mikrostrukturní stability v podmínkách zvýšené teploty hořčíkové slitiny AZ91 připravené pomocí metody ECAP. Mikrostrukturní stabilita byla zkoumána pomocí metody EBSD, která umožňuje zachycení změn velikosti zrn, změn vzájemného poměru LAB a HAB a lokální distorze krystalové mřížky pomocí parametru KAM . BYlo experimentálně zjištěno, že prahová hodnota teploty kdy dochází k významnému hrubnutí zrn je 350 stupnu Celsia. Pod touto teplotou nedochází ke změně střední velikosti zrna, nicméně dochází ke změnám v poměru mezi vysokoúhlovými a nízkoúhlovými hranicemi. Stejně tak bylo možno pozorovat změny v lokální distorzi krystalové mřížky.

Anglický abstrakt

The changes in microstructure of equal channel angular pressing (ECAP) processed magnesium alloy AZ91 during thermal exposure were studied in this paper. The microstructure stability was investigated by means of electron backscatter diffraction (EBSD), which allowed measuring the changes in grain size, mutual ratio of low-angle boundaries (LABs) to high-angle ones (HABs) and local lattice distortion evaluated by the kernel average misorientation (KAM) parameter. It was found experimentally that the threshold temperature at which significant grain coarsening takes place is 350 centigrade. No modification to mean grain diameter occur below this temperature, nonetheless, some changes in LAB and HAB fraction, as well as in local lattice distortion, can be observed.

Klíčová slova česky

Mikrostrukturní stabilita, hořčíková slitina AZ91, bezkontrakční úhlové protlačování (ECAP), střední jádrová dezorientace (KAM), EBSD

Klíčová slova anglicky

Microstructural stability, AZ91 magnesium alloy, Equal channel angular pressing (ECAP), Kernel average misorientation (KAM), Electron backscatter diffraction (EBSD)

Rok RIV

2015

Vydáno

09.07.2015

Nakladatel

Elsevier

ISSN

1044-5803

Ročník

107

Číslo

9

Strany od–do

167–173

Počet stran

7

BIBTEX


@article{BUT111291,
  author="Libor {Pantělejev} and Roman {Štěpánek} and Ondřej {Man},
  title="Thermal stability of bimodal microstructure in magnesium alloy AZ91 processed by ECAP",
  year="2015",
  volume="107",
  number="9",
  month="July",
  pages="167--173",
  publisher="Elsevier",
  issn="1044-5803"
}