Efekt isostatického lisování za tepla na nízkocyklovou únavu slitiny MAM-M-247 za teploty 900°C

ŠULÁK, I. OBRTLÍK, K. ŠKORÍK, V. HRBÁČEK, K.

Český název

Efekt isostatického lisování za tepla na nízkocyklovou únavu slitiny MAM-M-247 za teploty 900°C

Anglický název

EFFECT OF HIP ON LOW CYCLE FATIGUE OF MAR-M-247 AT 900°C

Typ

článek ve sborníku ve WoS nebo Scopus

Jazyk

en

Originální abstrakt

Polycrystalline nickel-base superalloy MAR-M-247 is used for high temperature applications requiring excellent combination of fatigue properties, creep resistance and surface stability. In the present work, the high temperature low cycle fatigue behaviour of cast nickel-base superalloy MAR-M-247 in as received condition and in hot isostatically pressed (HIP) condition was studied. The microstructure of the materials is characterized by dendritic grains, carbides and casting defects. Distribution and size of defects in both materials were studied. Beneficial effects of HIP process on cyclic stress-strain and fatigue life curves are discussed.

Český abstrakt

Polykrystalické niklová superslitina MAR-M-247 je používána na vysokoteplotní aplikace, které vyžadují vynikající kombinaci únavových vlastností, odolnost proti tečení a povrchovou stálost. V této práci, je studována vysokoteplotní nízkocyklová únava materiálu ve stavu po odlití MAR-M-247 a ve stavu po isostatickém lisování. Mikrostruktura materiálu se vyznačuje hrubou dendritickou strukturou s množstvím karbidů a licích vad. Distribuce a velikost vad v obou materiálech byly studovány. Příznívé účinky HIP procesu na napěťově deformační odezvu a únavovou životnost jsou diskutovány.

Anglický abstrakt

Polycrystalline nickel-base superalloy MAR-M-247 is used for high temperature applications requiring excellent combination of fatigue properties, creep resistance and surface stability. In the present work, the high temperature low cycle fatigue behaviour of cast nickel-base superalloy MAR-M-247 in as received condition and in hot isostatically pressed (HIP) condition was studied. The microstructure of the materials is characterized by dendritic grains, carbides and casting defects. Distribution and size of defects in both materials were studied. Beneficial effects of HIP process on cyclic stress-strain and fatigue life curves are discussed.

Klíčová slova anglicky

MAR-M247, High Temperature, Low Cycle Fatigue.

Rok RIV

2014

Vydáno

21.05.2014

Nakladatel

Tanger Ltd

Místo

Ostrava

ISBN

978-80-87294-54-3

Kniha

Metal 2014

Číslo edice

1

Strany od–do

1381–1386

Počet stran

6

BIBTEX


@inproceedings{BUT108535,
  author="Ivo {Šulák} and Karel {Obrtlík} and Viktor {Škorík} and Karel {Hrbáček},
  title="EFFECT OF HIP ON LOW CYCLE FATIGUE OF MAR-M-247 AT 900°C",
  booktitle="Metal 2014",
  year="2014",
  month="May",
  pages="1381--1386",
  publisher="Tanger Ltd",
  address="Ostrava",
  isbn="978-80-87294-54-3"
}