Hydrostatické válečkování aplikované na valivou plochu ložiska
ZEMČÍK, O. SEDLÁK, J. CHLADIL, J.
Český název
Hydrostatické válečkování aplikované na valivou plochu ložiska
Anglický název
Hydrostatic roller burnishing aplied on surface layer of bearing steel
Typ
článek ve sborníku ve WoS nebo Scopus
Jazyk
en
Originální abstrakt
The article describes observed changes in bearing steel due to roller burnishing. As the most suitable method for roller burnishing of hardened bearing steel was selected hydrostatic roller burnishing. The hydrostatic roller burnishing operation was apllied as an additional operation after standard finishing operations. All tests were performed on samples of material 100Cr6 (EN 10132-4) and changes in the surface layer of the workpiece are then evaluated. To get the best possible default parameters for tests several simulation, using finite element methods, were used. The main tested parameters included the residual stress and plastic deformation during roller burnishing.
Český abstrakt
Článek se zabýva změnami v ložiskové oceli po aplikaci válečkování. Jako nejvhodnější metoda pro válečkování kalené ložiskové oceli bylo zvoleno hydrostatické válečkování. Metoda hydrostatického válečkování byla aplikována jako přídavná operace po standardních dokončovacích operacích. Všechny testy byly aplikovány na vzrocích z oceli 100Cr6 (EN 10132-4) a následně byly vyhodnoceny změny v povrchové vrstvě. Pro zajištění co nejvěrnějších výsledků, byly provedeny simulace procesu metodou konečných prvků. Mezi hlavní testované parametry patřily zbytkové napětí v povrché vrztvě, množství zbytkového austenitu a plastická deformace.
Anglický abstrakt
The article describes observed changes in bearing steel due to roller burnishing. As the most suitable method for roller burnishing of hardened bearing steel was selected hydrostatic roller burnishing. The hydrostatic roller burnishing operation was apllied as an additional operation after standard finishing operations. All tests were performed on samples of material 100Cr6 (EN 10132-4) and changes in the surface layer of the workpiece are then evaluated. To get the best possible default parameters for tests several simulation, using finite element methods, were used. The main tested parameters included the residual stress and plastic deformation during roller burnishing.
Klíčová slova česky
ložisková ocel, válečkování, metoda konečných prvků, zbytkový austenit, zbytkové napětí
Klíčová slova anglicky
bearing steel, roller burnishing, finite element method, residual austenite, residual stress
Rok RIV
2014
Vydáno
25.04.2014
Nakladatel
Brno University of Technology
Místo
Technická 2896/2, 61669 Brno, Czech Republic
ISBN
978-80-214-4931-2
Kniha
ERIN 2014 Proceedings of Abstract
Strany od–do
1–8
Počet stran
8
BIBTEX
@inproceedings{BUT107443,
author="Oskar {Zemčík} and Josef {Sedlák} and Josef {Chladil},
title="Hydrostatic roller burnishing aplied on surface layer of bearing steel",
booktitle="ERIN 2014 Proceedings of Abstract",
year="2014",
month="April",
pages="1--8",
publisher="Brno University of Technology",
address="Technická 2896/2, 61669 Brno, Czech Republic",
isbn="978-80-214-4931-2"
}