Identifikace tvárného porušení a vliv vrubu na tahové vlastnosti oceli Eurofer97

Ductile damage identification and tensile notch effect for Eurofer97 steel

článek v časopise - ostatní, Jost

en

The effect of stress multiaxiality on void nucleation and growth at ductile fracture was studied for a Eurofer97 steel. Tensile testing of smooth and notched round bars was performed. The fractography and metallography analysis on broken halves of tensile bars together with the image analysis were carried out. The increasing stress multiaxiality in the bars lowers the strain at fracture. The ductile damage of the steel consists from the nucleation of the voids by decohesion mechanims, their gradual growth and finishes by rapid void coalescence. The increasing stress multiaxiality causes larger growth of voids together with observed restriction of void nucelation.

Byl studován vliv mulatiaxiality napětí na nukleaci a růst dutin při tvárném porušení pro ocel Eurofer97. Bylo realizováno zkoušení tahových vlastností oceli na hladkých a vrubovaných tahových tyčích. Poté byly provedeny na přelomených polovinách těles fraktografické a metalografické analýzy a současně byly výsledky těchto analýz zpracovány pomocí obrazové analýzy. Rostoucí multiaxialita napětí ve středu tahových tyčí způsobuje nižší lomové deformace. Na základě analýz bylo vyvozeno, že tvárné porušení oceli je realizováno prostřednictvím nukleace dutin dekohezním mechanismem částice/matrice, jejich následným růstem a rychlou koalescencí dutin jako finální fází procesu. Rostoucí multiaxialita napětí podporuje proce růstu dutin při současném potlačení procesu nuklace dutin.

The effect of stress multiaxiality on void nucleation and growth at ductile fracture was studied for a Eurofer97 steel. Tensile testing of smooth and notched round bars was performed. The fractography and metallography analysis on broken halves of tensile bars together with the image analysis were carried out. The increasing stress multiaxiality in the bars lowers the strain at fracture. The ductile damage of the steel consists from the nucleation of the voids by decohesion mechanims, their gradual growth and finishes by rapid void coalescence. The increasing stress multiaxiality causes larger growth of voids together with observed restriction of void nucelation.

Eurofer97, vrubované tahové tyče, dutiny, nukleace a růst

Eurofer97, notched tensile bars, voids, nucleation and growth