Poškození vícevrstvých polymerních materiálů při creepovém zatěžování
ZOUHAR, M. HUTAŘ, P. NÁHLÍK, L. KNÉSL, Z.
Český název
Poškození vícevrstvých polymerních materiálů při creepovém zatěžování
Anglický název
Damage of multilayer polymer materials under creep loading
Typ
článek v časopise - ostatní, Jost
Jazyk
en
Originální abstrakt
Failure of layered materials is frequently caused by the existence of interfaces between single layers. In structures loaded by long-term constant stress the damage can be described on micro-scale by material changes due to active creep mechanism and at the macro-level by a corresponding change of the stress and strain field. In the contribution the behavior of a crack propagating through the interface is analyzed. Primary attention is devoted to a crack with its tip at the interface under creep exposition. The step change of material properties at the bi-material interface means that standard fracture mechanics access is not applicable and a modified approach based on generalization of the classical concept has to be used. The approach is illustrated on the damage of a plastic pipe with protective layer.
Český abstrakt
V příspěvku je studován růst trhliny přes materiálovém rozhranní. Primární pozornost je věnována růstu trhliny s vrcholem na materiálovém rozhraní vystavené creepovému zatěžování. Díky skokové změně materiálových vlastností nemůže být použito přístupů standartní lomové mechaniky a využívá se modifikovaného přístupu založené na koncepci zobecněného součinitele intenzity napětí.
Anglický abstrakt
Failure of layered materials is frequently caused by the existence of interfaces between single layers. In structures loaded by long-term constant stress the damage can be described on micro-scale by material changes due to active creep mechanism and at the macro-level by a corresponding change of the stress and strain field. In the contribution the behavior of a crack propagating through the interface is analyzed. Primary attention is devoted to a crack with its tip at the interface under creep exposition. The step change of material properties at the bi-material interface means that standard fracture mechanics access is not applicable and a modified approach based on generalization of the classical concept has to be used. The approach is illustrated on the damage of a plastic pipe with protective layer.
Klíčová slova česky
CMOD, materiálové rozhranní, creep, lomová mechanika
Klíčová slova anglicky
CMOD, material interface, creep, fracture mechanics
Rok RIV
2011
Vydáno
05.01.2011
ISSN
1013-9826
Časopis
Key Engineering Materials
Ročník
2011
Číslo
465
Strany od–do
153–156
Počet stran
4
BIBTEX
@article{BUT49978,
author="Michal {Zouhar} and Pavel {Hutař} and Luboš {Náhlík} and Zdeněk {Knésl},
title="Damage of multilayer polymer materials under creep loading",
journal="Key Engineering Materials",
year="2011",
volume="2011",
number="465",
month="January",
pages="153--156",
issn="1013-9826"
}