Studium vzniku a omezení reoxidace kovu u odlitků ze slitin železa
ELBEL, T. ŠENBERGER, J. ZÁDĚRA, A.
Český název
Studium vzniku a omezení reoxidace kovu u odlitků ze slitin železa
Anglický název
Study of the occurrence and suppression of metal reoxidation in ferrous castings
Typ
článek v časopise - ostatní, Jost
Jazyk
en
Originální abstrakt
Recent advances in understanding the processes of casting metals into green sand moulds have shown that the occurrence of reoxidation plays a key role in the control of the quality of castings. The reoxidation gives rise to solid, liquid and gaseous products that may further react with the metal and the foundry mould, causing various surface and internal defects in the casting. The resultant occurrence of casting defects is affected by the content of deoxidation elements in the metal and by the process of deoxidation reactions in the mould during and after metal pouring. The present work deals with changes in oxygen activity in metal poured into sand moulds.
Český abstrakt
Důsledkem reoxidace jsou pevné, tekuté a plynné produkty, které mohou reagovat dále s kovem a slévárenskou formou za vzniku různých povrchových i vnitřních vad odlitku. Během reoxidace mohou vznikat následující vady odlitků : makrovměstky (struskové šumy, ceroxidy, sekundární struska); plynové dutiny (struskoplynové vady, bodliny, endogenní bubliny); mikrovměstky, chemická penetrace a strukturní anomálie.
Anglický abstrakt
Recent advances in understanding the processes of casting metals into green sand moulds have shown that the occurrence of reoxidation plays a key role in the control of the quality of castings. The reoxidation gives rise to solid, liquid and gaseous products that may further react with the metal and the foundry mould, causing various surface and internal defects in the casting. The resultant occurrence of casting defects is affected by the content of deoxidation elements in the metal and by the process of deoxidation reactions in the mould during and after metal pouring. The present work deals with changes in oxygen activity in metal poured into sand moulds.
Klíčová slova česky
reoxidace, ocelové odlitky, aktivita kyslíku
Klíčová slova anglicky
reoxidation, ferrous castings,oxygen activity
Rok RIV
2007
Vydáno
12.12.2007
ISSN
0046-5933
Časopis
International Foundry Research
Ročník
59
Číslo
4
Strany od–do
32–37
Počet stran
6
BIBTEX
@article{BUT43955,
author="Tomáš {Elbel} and Jaroslav {Šenberger} and Antonín {Záděra},
title="Study of the occurrence and suppression of metal reoxidation in ferrous castings",
journal="International Foundry Research",
year="2007",
volume="59",
number="4",
month="December",
pages="32--37",
issn="0046-5933"
}