Vliv naplynění a rychlosti tuhnutí na strukturu, porezitu a mechanické vlastnosti odlitků ze slitiny AlSi9Cu3

ROUČKA, J. VEVERKA, A. DIVIŠ, V. ŇUKSA, P.

Český název

Vliv naplynění a rychlosti tuhnutí na strukturu, porezitu a mechanické vlastnosti odlitků ze slitiny AlSi9Cu3

Anglický název

Effect of gassing and solidification rate on structure, porosity and mechanical properties of AlSi9Cu3 alloy castings

Typ

článek ve sborníku ve WoS nebo Scopus

Jazyk

en

Originální abstrakt

Test specimens of AlSi9Cu3 alloy cast in sand and metalic moulds were used to assess the extent of porosity in dependence on the gas content in the melt and on the solidification rate. On the basis of the dendrite arm spacing (DAS) the size of primary phases was evaluated and the mechanical properties of test pieces were measured. It has been proved that higher solidification rates contributes to greatly reduced porosity, smaller size of individual gas pores, finer structure, and higher strength and ductility of the alloy. The shape of pores is influenced by gas content significantly.

Český abstrakt

Na vzorcích ze slitiny AlSi9Cu3, odlévané do pískových a do kovových forem byl sledován rozsah porezity v závislosti na naplynění taveniny a rychlosti tuhnutí. Velikost dendritů primární fáze byla hodnocena pomocí kriteria DAS, na zkušebních vzorcích byly zjišťovány mechanické vlastnosti. Bylo zjištěno, že při zvýšení rychlosti tuhnutí se snižuje rozsah porezity, zmenšuje se velikost plynových pórů, zjemňuje struktura a zvyšuje se pevnost slitiny. Tvar pórů je významně ovlivněn stupněm naplynění taveniny.

Anglický abstrakt

Test specimens of AlSi9Cu3 alloy cast in sand and metalic moulds were used to assess the extent of porosity in dependence on the gas content in the melt and on the solidification rate. On the basis of the dendrite arm spacing (DAS) the size of primary phases was evaluated and the mechanical properties of test pieces were measured. It has been proved that higher solidification rates contributes to greatly reduced porosity, smaller size of individual gas pores, finer structure, and higher strength and ductility of the alloy. The shape of pores is influenced by gas content significantly.

Klíčová slova česky

Naplynění, porezita, rychlost tuhnutí, vzdálenost sekundárních os dendritů, mechanické vlastnosti

Klíčová slova anglicky

Porosity, cooling rate, dendrite arm spacing, mechanical properties

Rok RIV

2007

Vydáno

10.10.2007

Nakladatel

Trasactions of the Universities of Košice

Místo

Košice

Kniha

Aluminium 2007

Strany od–do

90–96

Počet stran

7

BIBTEX


@inproceedings{BUT23256,
  author="Jaromír {Roučka} and Aleš {Veverka} and Vladimír {Diviš} and Petr {Ňuksa},
  title="Effect of gassing and solidification rate on structure, porosity and mechanical properties of AlSi9Cu3 alloy castings",
  booktitle="Aluminium 2007",
  year="2007",
  month="October",
  pages="90--96",
  publisher="Trasactions of the Universities of Košice",
  address="Košice"
}