Publication detail
Properties of composites based on alkali-activated slag cured under high temperatures
ROVNANÍKOVÁ, P. BAYER, P.
Czech title
Vlastnosti kompozitů na bázi alkalicky aktivované strusky namáhaných vysokými teplotami
English title
Properties of composites based on alkali-activated slag cured under high temperatures
Type
conference paper
Language
cs
Original abstract
Jsou popsány vlastnosti kompozitů na bázi alkalicky aktivované strusky při zahřívání na teploty 200, 400, 600, 800 a 1000°C po dobu 1 hodiny. Výsledky ukazují, že do teploty 400°C nedochází k závažnému porušení mikrostruktury a ke snižování pevností. Zahřívání na teplotu 1000°C vedlo ke snížení pevnosti v tlaku na 30 % původní pevnosti. The properties of the composites based on alkali-activated blast furnace slag heated 1 hour at temperatures 200, 400, 600, 800 and 1000°C are described. The composite microstructure is stable to the temperature 400°C and compession strength is not significantly decreased. The temperature 1000°C caused compession strength decreasing to 30 % of the origial strength.
Czech abstract
Jsou popsány vlastnosti kompozitů na bázi alkalicky aktivované strusky při zahřívání na teploty 200, 400, 600, 800 a 1000°C po dobu 1 hodiny. Výsledky ukazují, že do teploty 400°C nedochází k závažnému porušení mikrostruktury a ke snižování pevností. Zahřívání na teplotu 1000°C vedlo ke snížení pevnosti v tlaku na 30 % původní pevnosti. The properties of the composites based on alkali-activated blast furnace slag heated 1 hour at temperatures 200, 400, 600, 800 and 1000°C are described. The composite microstructure is stable to the temperature 400°C and compession strength is not significantly decreased. The temperature 1000°C caused compession strength decreasing to 30 % of the origial strength.
English abstract
The properties of the composites based on alkali-activated blast furnace slag heated 1 hour at temperatures 200, 400, 600, 800 and 1000°C are described. The composite microstructure is stable to the temperature 400°C and compession strength is not significantly decreased. The temperature 1000°C caused compession strength decreasing to 30 % of the origial strength.
Keywords in English
slag, alkali-activation, composite, temperature, compression strength
RIV year
2001
Released
19.09.2001
Publisher
Ústav technologie stavebních hmot a dílců, Stavební fakulta VUT v Brně
Location
Brno
ISBN
80-214-1936-9
Book
CONSTRUMAT 2001. Konference o stavebních materiálech.
Edition number
1.
Pages count
7
BIBTEX
@inproceedings{BUT3416,
author="Pavla {Rovnaníková} and Patrik {Bayer},
title="Vlastnosti kompozitů na bázi alkalicky aktivované strusky namáhaných vysokými teplotami",
booktitle="CONSTRUMAT 2001. Konference o stavebních materiálech.",
year="2001",
month="September",
publisher="Ústav technologie stavebních hmot a dílců, Stavební fakulta VUT v Brně",
address="Brno",
isbn="80-214-1936-9"
}